The bending and shaping mold for iron pipes is made of Cr12MoV, and the product is always scratched. The master always calls for it, but using Yuhui ordered product DC53 has a much better effect, and the master no longer calls for it.
Mr. Hu, an old customer, came to buy 8566 die steel this morning. Taking this opportunity, I would like to ask him. By the way, your previous bend pipe mold used Cr12MoV, which was prone to scratches, but later you used our DC53. How is the usage? Has the scratch problem been improved?
The reply said, it’s much better.
I asked again, how many products are usually made now and how many molds are repaired? (Many mold makers buy mold steel and ask how many products can be made, so I am also interested in collecting data in this area)
The reply said, I need to ask about this. Previously, the master always said that he didn’t mention it to me after the replacement.
If the master stops calling, it means the problem has been solved. Otherwise, the mold will not work well, and the master will definitely call every day. Tools are not easy to use, whoever uses them will get angry, whoever uses them will shout.
There are some cases that I don’t want to talk about because when I say them, someone asks, ‘If you can’t earn two, there are a lot of things to do.’.
I am not sending this case for promotion, just to document my work experience.