It’s better not to do some business well, and for some people, it’s better to let them continue to hit the southern wall.
Mr. Jiang said that 2mm stainless steel punching material will cause PM23 to collapse. Now, using the four copied 856 die steel you mentioned, it will wear out after 10000 punches. The punch will wear down from 7.1mm to 7.2mm, and 30000 products will be punched per day. Two punches will be replaced every day, and dozens of punches will be cut at once. The mold has been changed to a quick release structure and replaced with your 8566. Will it be better? If it can be better, I will buy some and try it out.
The working conditions of this mold are quite detailed, and it can be recommended to use 8566 anti collapse tool steel. However, why should I join the fun and ask him to donate two taels of mold steel? I didn’t wait for your two taels of 8566 to last, so I asked him to continue using four copies of 8566, which is cheaper.
You have already tried two types of tool steel and changed the mold structure to quick release, so you are planning to replace the punch.
Just change the punch twice a day. Anyway, there’s nothing to do and nothing to do. The skill is yours, and you don’t need to hire anyone or spend money. Just cut dozens of punch heads at once. Anyway, the wire cutting machine is yours, and you don’t need to spend money. It’s still parked there.
Some people, you need to support them instead of changing them. When they come to consult with you, they just want to confirm with you that I am amazing. I have changed the mold structure, and you need to give them a thumbs up.
The use of 8566 die steel for punch cracking is a stark contrast between the old and new societies, and some people cannot experience it.
*************
Wu Dejian’s tool steel, the chief of staff of the user, bought everything he had used.