How to solve the problem of easily collapsing and sinking at the inlet position when using SKD61 with 30% nylon fiber?
Question from a netizen in the 286th live broadcast room: How to solve the problem of easily collapsing and sinking at the water inlet position when using SKD61 with 30% nylon fiber? Nylon reinforced plastic with 30% fibers has a very serious erosion effect on the mold, and it is necessary to use mold steel…
-
Books are useful
No matter how much information you read online, it’s better to read a related book. This is a sudden feeling. Recently, I have been learning about a certain field of knowledge. At first, I watched videos online, and the more I watched, the more confused I became. Later, after reading two books, I seemed to…
-
The terminal blade is prone to cracking with LG, you can try a small LG order
The terminal blades are made of mold steel, which is a bit small, but it’s good to have one order a day, dozens of pieces at a time. But in business, it’s impossible to use mathematical formulas to calculate. This batch of LG may seem small in size, but when processed into terminal blades, there…
-
There is no answer to doubling lifespan without increasing costs, and if there is, I won’t tell you.
The problem of doubling lifespan without increasing costs cannot be solved. Mr. Lin is engaged in hot rolling, hot cutting, and hot forming, including a clamp with a working temperature of 300 ℃. He currently uses H13 mold steel, but the sharp corners of the clamp are severely worn, causing slippage and a lifespan of…
-
Punch 8mm hot-rolled plate, M42 will collapse after 3000 punches, this is because the wrong tool steel was used. Chapter 576
The wrong material was used for the mold, and even the most expensive tool steel is useless. In the 275th live broadcast room, a netizen named Xiao Jinmao asked, ‘If you punch an 8mm hot plate in one step, M42 is prone to breakage and can only be punched 3000 times at a time.’. Stamping 8mm…
-
Record the first wave of customers who visit during the new year.
The first wave of customers for the new year came from Dalingshan, Dongguan. This customer has been in contact since the New Year. He works on aluminum cold heading molds and now uses DC53 die steel, which cracks the mold quickly and cannot produce the product. No matter how the mold is optimized, its lifespan…
-
8566 anti collapse steel, several hundred kilograms per piece, sold very well.
8566 anti collapse steel, several hundred kilograms per piece, sold very well. It’s strange to say that the more customers buy large items, the less verbose they are, and the more they buy small items, the more they pretend to be big shots. There are not many customers, just a few big whale customers are…
-
The product produced by stamping 6mm thick 20 steel with Cr12MoV has burrs, which is a material error. Notes on hand 070
If the wrong material is used for the mold, there will be various problems, and once misjudged, there will be various improper operations. Just now Mr. Liang came to ask, what are the characteristics of 8503 die steel, how to polish it, how can it be polished into a mirror surface, whether the mold is…
-
The terminal blade customer has come to purchase 50 pieces of high toughness LG die steel again, happy!
Today is a happy day. Chengdu customers have come to purchase high toughness LG die steel again, this time purchasing 50 pieces. Mr. Zhang purchased LG die steel in small quantities in December of the 25th year for trial use. At that time, he said that if LG’s toughness was really good and could indeed…
-
Is heat-resistant steel 8433 also suitable for forging high-temperature alloys?
A netizen who consulted 8566 asked me, is 8433 also suitable for high-temperature alloy forging? To be honest, the hardness of heat-resistant steel 8433 is 50-54HRC, which is a hot forging high-temperature alloy. The thermal wear performance of 8433 is slightly inferior. Although the heat resistance of 8433 is 2-3 times that of H13, its…